ASTM A335 P22 Alloy Steel Pipe
ASTM A335 P22 Alloy Steel Pipe
ASTM A335 P22 Alloy Steel Pipe

ASTM A335 P22 Alloy Steel Pipe

ASTM A335 P22 is the part of ASTM A335. ASTM A335 P22 alloy steel pipe shall be suitable for bending, flanging, and similar forming operations, and for fusion welding. The steel material shall conform to chemical composition, tensile property, and hardness requirements.Each length of pipe shall be subjected to the hydrostatic test. Also, each pipe shall be examined by a non-destructive examination method in accordance to the required practices.The range of ASTM A335 P22 pipe sizes that may be examined by each method shall be subjected to the limitations in the scope of the respective practice.

Send Message

Introduction

ASTM A335 P22 is the part of ASTM A335. ASTM A335 P22 alloy steel pipe shall be suitable for bending, flanging, and similar forming operations, and for fusion welding. The steel material shall conform to chemical composition, tensile property, and hardness requirements.Each length of pipe shall be subjected to the hydrostatic test. Also, each pipe shall be examined by a non-destructive examination method in accordance to the required practices.The range of ASTM A335 P22 pipe sizes that may be examined by each method shall be subjected to the limitations in the scope of the respective practice.

Outer Dimensions: 19.05mm – 114.3mm

Wall Thickness: 2.0mm – 14 mm

Length: max 16000mm

Steel grade: ASTM A335 P22 

 

Mechanical Tests Specified

Transverse or Longitudinal Tension Test and Flattening Test, Hardness Test, or Bend Test For material heat treated in a batch-type furnace, tests shall be made on 5% of the pipe from each treated lot. For small lots, at least one pipe shall be tested.

For material heat treated by the continuous process, tests shall be made on a sufficient number of pipe to constitute 5% of the lot, but in no case less than 2 pipe.

 

Notes for Bend Test

For pipe whose diameter exceeds NPS 25 and whose diameter to wall thickness ratio is 7.0 or less shall be subjected to the bend test instead of the flattening test.

Other pipe whose diameter equals or exceeds NPS 10 may be given the bend test in place of the flattening test subject to the approval of the purchaser.

The bend test specimens shall be bent at room temperature through 180 without cracking on the outside of the bent portion.

 

Related informations

European Standards for steel

ASTM Standards for steel pipes

JIS Seamless Pipe

Tubes for Mechanical and Automobile

ASTM A335 Pipe Specifications

ASTM A333 Pipe Specifications

Product Parameters

ASTM A335 P22 Chemical Composition
C, % Mn, % P, % S, % Si, % Cr, % Mo, %
0.015 max 0.30-0.61 0.025 max 0.025 max 0.50 max 1.90-2.60 0.87-1.13

 

ASTM A335 P22 Properties
Tensile Strength, MPa Yield Strength, MPa Elongation, %
415 min 205 min 30 min

 

ASTM A335 Gr P22 Equivalent Material
ASTM ASME Equivalent material JIS G 3458 UNS BS DIN ISO ABS NK LRS
A335 P22 SA335 P22 T22, 10CrMo910, 10CrMo9-10, 1.7380, 11CrMo9-10, 1.7383 STPA 24 K21590 3604 P1 622 17175 2604 II TS34 ABS 13 KSTPA 24 Sec 2
10CrMo910 2-1/4Cr1Mo410